西安建筑科技大學課程設計(論文)西安建筑科技大學課程設計(論文)西安建筑科技大學課程設計（論文）西安建筑科技大學課程設計（論文）Sn摻雜ZnO納米陣列的水熱合成摘要:以ZnCl2和NaOH為原料，用SnCl4-4H2O作摻雜劑，通過水熱法合成了5口摻雜ZnO納米顆粒。利用X射線衍射(XRD)、場發射掃描電鏡(FE-SEM)、紫外-可見吸收光譜(UV-Vis)及光致發光(PL)光譜等測試技術對樣品的物相、形貌及光學性能進行了表征。結果表明:制得的Sn摻雜ZnO納米粒子具有六角纖鋅礦結構。隨著錫摻雜濃度的增大，納米晶的平均粒度增加，晶體形貌由短棒狀向單錐和雙錐狀變;提高前驅液的pH值，所得樣品的形貌由長柱狀向短柱狀轉變。室溫下，觀測到三個光致發光帶一個峰值在433nm處的強紫光發射峰，一個約在401nm處的近紫外發光峰及一個^66nm處的弱藍光發光峰。在實驗摻雜濃度范圍內，Sn的摻雜致使改變納米ZnO的發光強度，對發光峰位置影響不大。關鍵詞：ZnO納米晶;水熱合成;Sn摻雜;光學性能Abstract:HydrothermalsynthesisofSndoped

ZnOnanoarrayAbstract:Sn-dopedZnOnanocrystalsweresynthesizedbythehydrothermalmethodusingZnCl2andNaOHasrawmaterialsat200efor5h.ThedopantsourceoftinwasSnCl4?4H2Oandtheatomicpercentageofdopantinthesolutionweren(Sn):n(Zn)=1%and2%respectively.Thephasecomposition,morphology,sizeaswellasopticalpropertiesofthesamplshavebeencharacterizedbymeansofX-raydiffraction(XRD),fieldemissionscanningelectronmicroscopy(FE-SEM),UV-Visibleabsorptionandphotoluminescence(PL)spectra.TheeffectsoftheSndopingconcentrationandthepHvalueoftheprecursorsolutiononthesurfacemorphologyandopticalpropertiesofthesampleshavealsobeenstudied.TheexperimentalresultsindicatethattheobtainedSn-dopedZnOnanocrystalsareofhexagonalwurtzitestructure.Theaveragegrainsizeofthesamplesincreasesandthesurfacemorphologygoesfromshortrod-liketosinglecone-likeanddoublecone-likewiththeincreaseofSnconcentration.Inaddition,thesurfacemorphologyofthesamplescanalsobeaffectedbythebasicityoftheprecursorsolution.Sinceitchangesfromlongrod-like(forpH7.0)toshortrod-like(forpH12.0).TherewasaUVabsorptionpeakfromtheUV-visibleabsorptionspectrawhichhaveared-shiftwiththeincreaseofSnconcentration.Threephotoluminescencebands,includingastrongpurpleemissionat433nm,alef-tshouldernearUVbandemissionaround401nmaswellasaweakblueemissionat466nmwereobservedatroomtemperature.TheintensitiesoftheemissionpeaksincreasedwiththeincreaseofSnconcentration.ComparedwiththatofundopedZnOnanocrysta,lonlytheintensitiesofemissionpeaksarechanged,butthepeakpositionsarealmostnotchangedintheSndopingconcentrationrangofourexperiments.KeyW0rds幺口。nanocrysta;lhydrothermalsynthesis;Sn-doping;opticalproperties目錄口TOC\o"1-5"\h\z.引言 1.實驗 2樣品的制備 2樣品的表征 2.結果與討論 31X射線衍射(XRD)分析 3\o"CurrentDocument"形貌分析 5\o"CurrentDocument"紫外可見吸收光譜和光致發光分析 6\o"CurrentDocument".結論 9\o"CurrentDocument"參考文獻 10\o"CurrentDocument"致 謝 13西安建筑科技大學課程設計（論文）西安建筑科技大學課程設計（論文）西安建筑科技大學課程設計（論文）第第#頁共17頁致謝本文是云老師的指導下完成的。感謝云老師在百忙之中對我的多次指導關懷，在課題試驗過程中及論文撰寫過程中，老師給予很大幫助。每次遇到困難，老師都能伸出援助之手，特別讓感動的是老師在論文修