Q690鋼焊接HQ690高強度鋼為研究對象，探究其焊接H形截面殘余應力及其對軸壓構件整體穩定性能的影響。通過實驗測試和有限元分析得出：Q690H形截面存在一定的殘余應力，關鍵詞：Q690鋼；焊接殘余應力；HWiththewidespreadapplicationofsteelstructuresinbridges,aerospaceandotherfields,thestudyoftheoverallstabilityofsteelstructuresisbecomingmoreandmoreimportant.ThispapertakesQ690high-strengthsteelastheresearchobject,andexplorestheresidualstressofweldedH-sectionsanditsimpactontheoverallstabilityofaxialcompressionmembers.Throughexperimentaltestsandfiniteelementanalysis,itisfoundthattherearecertainresidualstressesintheweldedH-sectionsofQ690steel,andthesestressesaredistributedunevenlyandconcentratedneartheweld.Theseresidualstresseshaveanimpactontheoverallstabilityofaxialcompressionmembers,whichchangesthefailuremodefromglobalfailuretolocalfailure,andthefailurelocationmaynotnecessarilyappearneartheweld.Inthedesignprocessofaxialcompressionmembers,itisnecessarytoconsidertheinfluenceofweldingresidualstresstoensuretheoverallstabilityperformanceofthemembers.Keywords:Q690steel;weldingresidualstress;H-section;axialcompressionmember;overallstability.Q90應用于建筑、橋梁、航空航天等領域。而焊接是鋼結構中常用的連接方式之一，但是焊接會產生殘余應力，可能對構件的穩定性能造成影響。Q90H形截面殘余應力及其對軸壓構件整體穩定性能影響是非常有必要的。Q90H形截面構件進行實驗測L500m、1000mm、150mm2000m用自動焊接工藝進行焊接。實驗測試采用板剪法，通過測量構件在施加不同荷載下的變形量和應變值，計算出標準化彎矩和標準化剪力，推導H形截面的強度和剛度特性。實驗測試結果表明，不同長度的焊接H形截面都存在一定的殘余應1L=1500mm的焊接H形截面殘余應力分布情況。1L=1500mmHQ690H形截面殘余應力對軸壓構件整建立了L=1500mm的焊接H形截面軸壓構件有限元模型，如圖2SHELL181有限元單元，仿真分析了構件在施加不同荷載2L=1500mmHH形截面殘余應力對軸壓構件整體穩定素來決定。圖3展示了構件在不同荷載作用下的破壞模式和破壞位置。3Q690H形截面存在一定的殘余應力，這些應力分布不在軸壓構件的設計過程中，需要考慮到焊接殘余應力的影響，以保證構件的整體穩定性能。曹緒豐焊接殘余應力對鋼結構整體穩定性的影響研究[D