ICS91.120.10

DB

遼寧省地方標準

DB21/Txxxx-2021

P32備案號J-2021

遼寧省抗冰防滑瀝青路面設(shè)計與施工技

術(shù)規(guī)程

Liaoningprovinceiceantiskidasphaltpavement

designandconstructiontechnologyprocedures

（送審稿）

2021-XX-XX發(fā)布2021-XX-XX實施

遼寧省住房和城鄉(xiāng)建設(shè)廳

聯(lián)合發(fā)布

遼寧省市場監(jiān)督管理局

目次

前言.............................................錯誤!未定義書簽。再

1總則...........................................................5i

2規(guī)范性引用文件..................................................62

3術(shù)語、符號和定義................................................73

3.1術(shù)語......................................................73

3.2符號和定義................................................84

4原材料.........................................................96

4.1一般規(guī)定.................................錯誤!未定義書簽。6

4.2集料......................................錯誤!未定義書簽。6

4.3低冰點填料................................錯誤!未定義書簽。6

4.4瀝青、穩(wěn)定劑及填料........................錯誤!未定義書簽。？

5熱拌低冰點瀝青混合料............................錯誤!未定義書簽。8

5.1一般規(guī)定.................................錯誤!未定義書簽。8

5.2路面結(jié)構(gòu)組合..............................錯誤!未定義書簽。8

5.3材料規(guī)格及技術(shù)要求.......................錯誤!未定義書簽。9

5.4低冰點瀝青混合料配合比設(shè)計..............錯誤!未定義書簽。口

5.5低冰點瀝青混合料的拌制與儲存.............錯誤!未定義書簽。生

5.6低冰點瀝青混合料的運輸...................錯誤!未定義書簽。4a

5.7低冰點瀝青混合料的攤鋪與壓實............錯誤!未定義書簽。典

5.8開放交通及其他...........................錯誤!未定義書簽。43

5.9施工質(zhì)量管理.............................錯誤!未定義書簽。13

6低冰點瀝青路面含砂霧封層材料..................................184§

6.1一般規(guī)定.................................錯誤!未定義書簽。一

6.2低冰點含砂霧封層材料設(shè)計.................錯誤!未定義書簽。共

6.3低冰點含砂霧封層材料施工養(yǎng)護............錯誤!未定義書簽。共

6.4施工質(zhì)量管理與驗收.......................錯誤!未定義書簽。共

7低冰點瀝青路面微表處材料.......................錯誤!未定義書簽。微

7.1一般規(guī)定................................錯誤!未定義書簽。一

7.2低冰點微表處材料設(shè)計....................錯誤!未定義書簽。備

7.3低冰點微表處材料施工養(yǎng)護................錯誤!未定義書簽。的

7.4施工質(zhì)量管理與驗收.......................錯誤!未定義書簽。阻

8低冰點瀝青路面超薄磨耗層材料..................................2633

8.1一般規(guī)定...............................................2623

8.2低冰點超薄磨耗層材料設(shè)計...............................2633

8.3低冰點超薄磨耗層材料施工養(yǎng)護...........................2724

8.4施工質(zhì)量管理與驗收.....................................282&

附錄A.................................................................................................................................302^

冰-路界面粘結(jié)力試驗方法..........................................30?

A.1儀器與材料...............................................30?

A.2試驗方法與步驟...........................................30?

A.3結(jié)果整理.................................................3027

1

附錄B...........................................................3138

低冰點瀝青混合料冰點試驗方法.....................................3138

B.1儀器和材料...............................................3128

B.2試件準備.................................................312§

B.3初定冰點試驗方法與步驟...................................313§

B.4確定冰點試驗方法與步驟..................................312§

附錄C...........................................................322?

氯離子含量試驗方法...............................................323?

C.1儀器與材料..............................................323?

C.2試驗方法與步驟...........................................323?

C.3結(jié)果計算與評定..........................................322?

附錄D...........................................................3330

耐熱性指數(shù)試驗方法...............................................3330

D.1儀器與材料..............................................3330

D.2試驗方法與步驟...........................................3330

D.3結(jié)果計算................................................3330

附錄E...........................................................34S1

融冰率試驗方法...................................................34S4

E.1儀器和材料..............................................蹌共

E.2試驗方法與步驟...........................................34^

E.3結(jié)果計算與評定..........................................送共

附錄F...........................................................3533

高溫動水沖刷后殘留穩(wěn)定度比試驗方法...............................3533

F.1儀器和材料..............................................353S

F.2試驗方法與步驟...........................................3533

F.3結(jié)果計算與評定..........................................3533

附錄G...........................................................3633

高溫動水沖刷后毛體積相對密度變化率...............................3633

G.1儀器和材料..............................................3633

G.2試驗方法與步驟...........................................3633

G.3結(jié)果計算與評定...........................................3633

2

preface.........................................錯誤!未定義書簽。

1GeneralProvisions.............................................54

2Normativereferencedocuments..................................62

3Terms,symbols,anddefinitions................................7S

3.1Terms.......................................................7S

3.2symbols,anddefinitions...................................84

4Therawmaterials...............................................96

4.1Generalprovisions.........................錯誤!未定義書簽。6

4.2Aggregate..................................錯誤!未定義書簽。6

4.3Lowfreezingpointpacking................錯誤!未定義書簽。6

4.4Bitumen,stabilizerandfiller............錯誤!未定義書簽。？

5Hotmixlowfreezingpointasphaltmixture.....錯誤!未定義書簽。8

5.1Generalprovisions........................錯誤!未定義書簽。8

5.2Pavementstructurecombination...........錯誤!未定義書簽。8

5.3Materialspecificationandtechnicalrequirements錯誤！未定義書

簽。9

5.4Mixproportiondesignoflowfreezingpointasphaltmixture.錯

誤!未定義書簽。口

5.5Mixingandstorageoflowfreezingpointasphaltmixture錯誤！

未定義書簽。工

5.6Transportoflowfreezingpointasphaltmixture錯誤！未定義書簽。

42

5.7Pavingandcompactionoflowfreezingpointasphaltmixture...

.................................................錯誤!未定義書簽。一

5.8Opentotrafficandothers................錯誤!未定義書簽。43

5.9Constructionqualitymanagement...........錯誤!未定義書簽。43

6Sandmistsealingmaterialforlowfreezingpointasphaltpavement

.................................................................184§

6.1Generalprovisions.......................錯誤!未定義書簽。4■&

6.2Designoflowfreezingpointsandmistsealmaterial錯誤！未定

義書簽。養(yǎng)

6.3Constructionandmaintenanceoflowfreezingpointsandmist

sealingmaterial.................................錯誤!未定義書簽。技

6.4Constructionqualitymanagementandacceptance錯誤！未定義書簽。

7Microsurfacematerialoflowfreezingpointasphaltpavement錯誤！

未定義書簽。轉(zhuǎn)

7.1Generalprovisions.......................錯誤!未定義書簽。48

7.2Lowfreezingpointmicrosurfacematerialdesign錯誤！未定義書

簽。

7.3Lowfreezingpointmicrosurfacematerialconstruction

maintenance.....................................錯誤!未定義書簽。一

7.4Constructionqualitymanagementandacceptance...............

.................................................錯誤!未定義書簽。阻

3

8Ultra-thinwearlayermaterialforlowfreezingpointasphaltpavement

.......................................................................263S

8.1Generalprovisions...........................................262S

8.2Lowfreezingpointultra-thinwearlayermaterialdesign..262S

8.3Constructionandmaintenanceofultra-thinwearlayermaterials

withlowfreezingpoint.............................................2724

8.4Constructionqualitymanagementandacceptance..............2825-

TheappendixA........................................................302?

Testmethodforadhesionatice-roadinterface.....................302?

A.1InstrumentsandMaterials........................................

.......................................................................302^

A.2Testmethodsandprocedures..................................302Z

A.3Resultsof.....................................................302?

TheappendixB........................................................31.2S

Testmethodforfreezingpointoflowfreezingpointasphaltmixtures

.......................................................................3138

B.1InstrumentsandMaterials.......................................

.......................................................................313S

B.2Specimenpreparation.........................................31.28

B.3Testmethodandprocedureforinitialfreezingpoint......312^

B.4Determinefreezingpointtestmethodandprocedure........313§-

TheappendixC.......................................................322^

Testmethodforchlorideioncontent...............................3229

C.1InstrumentsandMaterials........................................

.......................................................................323?

C.2Testmethodsandprocedures..................................323?

C.3Calculationandevaluationofresults.......................322?

TheappendixD........................................................3330

Testmethodforthermalindex.......................................3330

D.1InstrumentsandMaterials.......................................

.......................................................................3330

D.2Testmethodsandprocedures...................................3330

D.3Calculationofresults

.......................................................................3330

TheappendixE........................................................34共

Testmethodformeltingrate........................................3434-

E.1Instrumentsandmaterials........................................

.......................................................................34S4

E.2Testmethodsandprocedures...................................3434

E.3Calculationandevaluationofresults.......................34共

TheappendixF........................................................35S2

Testmethodforresidualstabilityratioafterhightemperaturedynamic

waterscouring.......................................................3532

F.1Instrumentsandmaterials...................................3532

4

F.2Testmethodsandprocedures................................3533-

F.3Calculationandevaluationofresults......................3532

TheappendixG....................................................363S

Changerateofrelativedensityofhairvolumeafterhightemperature

dynamicwaterscouring...........................................36SS

G.1Instrumentsandmaterials..................................363S

G.2Testmethodsandprocedures................................363S

G.3Calculationandevaluationofresults......................363S

1總則

1.0.1為保證低冰點瀝青路面的工程質(zhì)量，特制訂本標準。

1.0.2本標準適用于各等級公路新建、改擴建和養(yǎng)護工程。

1.0.3低冰點瀝青路面設(shè)計與施工必須符合國家環(huán)境和生態(tài)保護的規(guī)定。

1.0.4低冰點路面主要適用于降雪地區(qū)。

1.0.5低冰點瀝青路面設(shè)計與施工除應(yīng)符合本標準外，尚應(yīng)符合國家頒布現(xiàn)行有關(guān)標

準、規(guī)范的規(guī)定。特殊地質(zhì)條件和地區(qū)的低冰點瀝青路面，可根據(jù)實際情況，制定補充規(guī)定。

5

2規(guī)范性引用文件

下列文件對于本指南的應(yīng)用是必不可少的。凡是注日期的引用文件，僅注日期的版本適

用于本文件；凡是不注日期的引用文件，其最新版本（包括所有的修改版）適用于本文件。

JT/T973路用非氯有機融雪劑

JTGE20公路工程瀝青及瀝青混合料試驗規(guī)程

JTGF40公路瀝青路面施工技術(shù)規(guī)范

JTGE42公路工程集料試驗規(guī)程

JTG3450公路路基路面現(xiàn)場測試規(guī)程

JT/T1210.2公路瀝青混合料用融冰雪材料第2部分：鹽化物材料

JTGD50公路瀝青路面設(shè)計規(guī)范

JTGH10公路養(yǎng)護技術(shù)規(guī)范

CJJ1城鎮(zhèn)道路施工與質(zhì)量驗收規(guī)范

CJJ169城鎮(zhèn)道路路面設(shè)計規(guī)范

CJJ36城鎮(zhèn)道路養(yǎng)護技術(shù)規(guī)范

CJJ2城市橋梁工程施工與質(zhì)量驗收規(guī)范

6

3術(shù)語、符號和定義

3.1術(shù)語

3.1.2

低冰點填料-Aanti-icingfiller

以冰點下降劑、憎水劑等材料經(jīng)物理與化學(xué)混合而制成的具有抗凝冰及降低冰-路界面

粘結(jié)強度功能的粉末狀材料。

3.1.3

無機類低冰點填料inorganicanti-icingfiller

以氯化鈉或氯化鈣等無機鹵鹽化學(xué)物質(zhì)為有效成分的低冰點填料。

3.1.4

有機類低冰點填料organicanti-icingfiller

以有機酸根離子等有機鹽類化學(xué)物質(zhì)為有效成分的低冰點填料。

3.1.5

低冰點含砂霧封層材料anti-icingsealcoatwithsand

以低冰點填料、乳化瀝青為主要成分的霧封層材料與砂組成的混合料。

3.1.6

低冰點微表處材料anti-icingmicro-surfacing

用具有一定級配的石屑或砂、填料（低冰點填料、水泥、石灰、粉煤灰、石粉等）與聚合

物改性乳化瀝青、外摻劑和水，按一定比例拌制成流動型混合料。

3.1.7

低冰點超薄磨耗層材料anti-icingsuperthinwearingcourse

以瀝青、石料、低冰點填料等材料拌和而成的用于超薄磨耗層的瀝青混合料。

3.1.8

低冰點瀝青混合料anti-icingasphaltmixture

以瀝青、石料、低冰點填料等材料拌和而成的混合料。

3.1.9

融冰率meltingicerate

將一定質(zhì)量的冰放置于瀝青混合料試件表面,在一定低溫條件下靜置一定時間后冰轉(zhuǎn)化

為水損失的質(zhì)量占原冰質(zhì)量的百分比。

3.1.10

7

耐熱性指數(shù)heattoleranceindex

高溫作用與常溫作用下低冰點填料水溶液濃度差的差值。

3.1.11

路面冰點freezingpointofpavement

路面內(nèi)水的凝固點。

3.1.12

鹽分釋出量saltreleaseamount

將直徑為101.6mm的標準低冰點瀝青混合料馬歇爾試件浸入1000ml蒸儲水中，分別測

試浸入10分鐘與24小時后液體的鹽分濃度，以二者差值計算試件的鹽分釋出量。

3.1.13

吸濕率moistureabsorption

將直徑為101.6mm的標準低冰點瀝青混合料馬歇爾試件，在105℃±5℃恒溫干燥2h,

稱重后，直接放置于恒溫恒濕箱中25℃、85%相對濕度條件下保溫24h,再次稱重，計算試

件的吸濕率。

3.1.14

冰-路界面粘結(jié)力bondforceoficeroadinterface

通過拉伸試驗測試得出的冰和瀝青混合料表面粘接的最大破壞力。

3.2符號和定義

AIF-低冰點填料

IAIF—無機類低冰點填料

0AIF—有機類低冰點填料

AAM一低冰點瀝青混合料

C—溶液離子濃度

A—接觸面積

PA-噴灑型陰離子乳化瀝青

PC-噴灑型陽離子乳化瀝青

FS—粘結(jié)強度

HTIc—耐熱性指數(shù)

々一b實驗條件下溶液鹽離子濃度

FP—冰點

4C一溶液鹽離子濃度差

SBR一苯乙烯-丁二烯橡膠（丁苯橡膠）之略語

MIR—融冰率

8

4原材料

4.1一般規(guī)定

4.1.1低冰點瀝青混合料使用的各種材料運至現(xiàn)場后必須取樣進行檢驗，經(jīng)第三方行業(yè)檢測

機構(gòu)評定合格后方可使用，不得以供應(yīng)商提供的檢測報告或商檢報告代替現(xiàn)場檢測。

4.1.2低冰點瀝青路面集料的選擇應(yīng)經(jīng)過嚴格的料源調(diào)查，料源質(zhì)量應(yīng)符合使用與環(huán)保要求,

若料源質(zhì)量不符合要求，應(yīng)通過適當處理使其滿足相關(guān)要求后使用。

4.1.3集料粒徑規(guī)格以方孔篩為準。不同料源、品種、規(guī)格的集料不得混雜堆放。

4.1.4低冰點填料應(yīng)存放于干燥、獨立、潔凈處，避免低冰點填料由于吸濕作用等導(dǎo)致自

身相關(guān)性能下降。

4.2集料

集料應(yīng)符合CJJ1-2008規(guī)范8.1.7條相關(guān)規(guī)定，以上規(guī)范如有更新則遵照最新版本執(zhí)行。

4.3低冰點填料

瀝青路面用低冰點填料必須經(jīng)行業(yè)檢測機構(gòu)產(chǎn)品認證，低冰點填料的原料應(yīng)干燥、潔凈，

能自由地從礦粉倉流出，其質(zhì)量應(yīng)符合表4.3-1-4.3-2的相關(guān)要求。

表4.3-1無機類低冰點填料質(zhì)量要求

試驗項目單位技術(shù)要求

外觀—粉末狀顆粒，無團粒結(jié)塊

氯離子含量%237

耐熱性指數(shù)%W0.5

表觀相對密度一21.7

含水率%W1

碳鋼腐蝕率mm/年<0.11

植物種子相對受害率%W15

貯存穩(wěn)定性%小于5%

0.6mm100

0.3mm—

篩孔通過率%

0.15mm90~100

0.075mm75-100

表4.3-2有機類低冰點填料質(zhì)量要求

項目單位技術(shù)要求

外觀—粉末狀顆粒，無團粒結(jié)塊

項目單位技術(shù)要求

耐熱性指數(shù)%W0.5

相對密度一21.7

含水率%W1

碳鋼腐蝕率mm/年W0.11

植物種子相對受害率%W15

9

貯存穩(wěn)定性%小于5%

0.6mm%100

0.3mm—

篩孔通過率

0.15mm90~100

0.075mm75~100

4.4瀝青、穩(wěn)定劑及填料

道路瀝青、乳化瀝青、纖維穩(wěn)定劑及填料均應(yīng)符合CJJ1-2008規(guī)范8.1.7條相關(guān)規(guī)定,

以上規(guī)范如有更新版本則遵照新版本執(zhí)行。

10

5熱拌低冰點瀝青混合料

5.1一般規(guī)定

5.1.1熱拌低冰點瀝青混合料適用于各種等級公路的瀝青路面，不宜采用OGFC等大空隙的

瀝青混合料，宜采用SMA、AC等密實級配瀝青混合料。

5.1.2熱拌低冰點瀝青混合料應(yīng)滿足表面功能需求，便于施工，不易離析。熱拌低冰點瀝青

混合料的施工應(yīng)與其下承層連續(xù)施工，并緊密連接成為整體。

5.1.3熱拌低冰點瀝青混合料的壓實度，針對城市快速路、主干路應(yīng)不小于96%,針對次

干路、支路、巷路等應(yīng)不小于95%。

5.1.4熱拌低冰點瀝青混合料的設(shè)計厚度應(yīng)根據(jù)所用集料的公稱最大粒徑確定。針對密集

配低冰點瀝青混合料，設(shè)計厚度應(yīng)不小于集料公稱最大粒徑的2.5?3倍；針對瑪蹄脂低冰

點瀝青混合料，設(shè)計厚度應(yīng)不小于集料公稱最大粒徑的2?2.5倍。

5.1.5熱拌AC類低冰點瀝青混合料中低冰點填料用量不宜小于礦料總質(zhì)量的4%,熱拌SMA

類低冰點瀝青混合料中低冰點填料用量不宜小于礦料總質(zhì)量的4%,且不宜大于礦料總質(zhì)量

的50%o

5.1.6熱拌低冰點瀝青混合料的生產(chǎn)應(yīng)配備獨立的低冰點填料添加倉，以實現(xiàn)低冰點填料的

準確計量，保證材料的質(zhì)量穩(wěn)定。

5.1.7熱拌低冰點瀝青混合料種類按集料公稱最大粒徑、礦料級配、空隙率劃分，分類見表

5.1.7o

表5.1.7熱拌低冰點瀝青混合料種類

密級配公稱最大粒

混合料類型最大粒徑(mm)

瀝青混凝土瀝青瑪蹄脂碎石徑(mm)

中粒式AC-16SMA-1616.019.0

AC-13SMA-1313.216.0

細粒式

AC-10SMA-109.513.2

砂粒式AC-5一4.759.5

設(shè)計空隙率(%)3-5%3-4%一一

5.1.8符合CJJ1-2008規(guī)范8.2.1~8.2.3、8.5.1條相關(guān)規(guī)定。

5.2路面結(jié)構(gòu)組合

5.2.1低冰點瀝青路面的基層類型可選擇無機結(jié)合料穩(wěn)定類基層、瀝青穩(wěn)定類基層和粒料

類基層。

5.2.2低冰點瀝青路面結(jié)構(gòu)組合可按表5.2.2選擇。

表5.2.2低冰點瀝青路面結(jié)構(gòu)組合

結(jié)構(gòu)組合交通量等級

面層組合上面層上基層下基層重中輕

無機結(jié)合料穩(wěn)定類VVV

無機結(jié)合料穩(wěn)定類

粒料類XVV

兩層式厚度不超過

無機結(jié)合料穩(wěn)定類VV

W15cm5cm

瀝青穩(wěn)定類瀝青穩(wěn)定類VVV

粒料類XXV

11

粒料類粒料類XXV

無機結(jié)合料穩(wěn)定類VVX

無機結(jié)合料穩(wěn)定類

粒料類XVX

三層厚度不超過

無機結(jié)合料穩(wěn)定類VX

式＞15cm5cm

瀝青穩(wěn)定類瀝青穩(wěn)定類VX

粒料類XVX

注：，表示推薦采用，義表示不推薦采用

5.3材料規(guī)格及技術(shù)要求

5.3.1本規(guī)范采用馬歇爾試驗配合比設(shè)計方法，熱拌低冰點瀝青混合料馬歇爾技術(shù)要求應(yīng)符

合表5.3.1-1-5.3.1-2的規(guī)定，并有良好的施工性能。當采用其他方法設(shè)計瀝青混合料時,

應(yīng)按本規(guī)范規(guī)定進行馬歇爾試驗及各項配合比設(shè)計檢驗，并報告不同設(shè)計方法的試驗結(jié)果。

表5.3.1-1密級配低冰點瀝青混凝土馬歇爾試驗技術(shù)標準

試驗指標技術(shù)要求

擊實次數(shù)(雙面)75次

試件尺寸6101.6mmX63.5mm

空隙率VV3~5%

穩(wěn)定度MS不小于8kN

相應(yīng)于以下公稱最大粒徑(mm)的最小VMA

設(shè)計空隙率

及VFA技術(shù)要求觥)

(%)

礦料間隙率1613.29.54.75

VMA(%)，不小于312.5131416

413.5141517

514.5151618

瀝青飽和度VFA觥)65-7570?85

表5.3.1-2SMA低冰點混合料馬歇爾試驗技術(shù)標準

試驗指標技術(shù)要求試驗方法

馬歇爾試件尺寸6101.6mmX63.5mmJTGE20-2011T0702

馬歇爾試件擊實次數(shù)雙面擊實50次JTGE20-2011T0702

空隙率VV3?4%JTGE20-2011T0705

礦料間隙率VMA,不小于17%JTGE20-2011T0705

粗集料骨架間隙率VCAmax,不大于VCADRCJTGE20-2011T0705

謝倫堡瀝青析漏試驗的結(jié)合料損失不大于0.1%JTGE20-2011T0732

肯塔堡飛散試驗的混合料損失或浸水飛散試驗不大于15%JTGE20-2011T0733

5.3.2熱拌低冰點瀝青混凝土在進行配合比設(shè)計時，需要在配合比設(shè)計的基礎(chǔ)上按下列方面

進行低冰點瀝青混合料抗冰融雪性能的檢驗。不符合要求的低冰點瀝青混合料，須更換材料

或重新進行配合比設(shè)計。

a)必須在規(guī)定的試驗條件下進行低冰點瀝青混合料冰點試驗，并符合表5.3.2-1的要

求，試驗方法見附錄B。氣候分區(qū)參見JTGF40規(guī)范附錄A執(zhí)行。

表5.3.2-1低冰點瀝青混合料冰點技術(shù)要求

12

低溫氣候區(qū)

項目單位

冬溫區(qū)冬冷區(qū)冬寒區(qū)冬嚴寒區(qū)

冰點℃不大于-5不大于-8不大于T2

b）必須在規(guī)定的試驗條件下進行低冰點瀝青混合料抗冰融雪能力試驗，并符合表

5.3.2-2的要求，試驗方法見附錄A、附錄C、附錄E。

表5.3.2-2低冰點瀝青混合料抗冰融雪能力技術(shù)要求

項目單位技術(shù)標準

融冰率%23

鹽分釋出量%<0.3

冰-路界面粘結(jié)強度kN<0.3

5.3.3必須在規(guī)定的試驗條件下進行低冰點瀝青混凝土長效性的試驗，并符合表5.3.3的要

求。

表5.3.3低冰點瀝青混合料長效性技術(shù)要求

項目單位技術(shù)標準

前五日累計釋放量mol/LW0.045

5.3.4對于公稱最大粒徑大于或等于9.5mm,且小于16.0mm的低冰點瀝青混合料（含AC類、

SMA類），需在配合比設(shè)計的基礎(chǔ)上按下列步驟進行高溫性能檢驗，技術(shù)要求見表5.3.4。氣

候分區(qū)參見JTGF40規(guī)范附錄A執(zhí)行。

表5.3.4低冰點瀝青混合料高溫性能技術(shù)要求

氣候條件與技術(shù)指標相應(yīng)于下列氣候分區(qū)所要求的動穩(wěn)定度（次/mm）

>3020?30<20

七月平均最高氣溫（℃）試驗方法

1.夏炎熱區(qū)2.夏熱區(qū)3.夏涼區(qū)

及氣候分區(qū)

1-11-21-31-42-12-22-32-43-2

普通瀝青混合料8001000600800600

JTGE20-2011

改性瀝青混合料24002800200024001800

T0719

SMA混合料3000

5.3.5對于低冰點瀝青混合料，需在配合比設(shè)計的基礎(chǔ)上進行水穩(wěn)定性檢驗，并滿足表

5.3.5-1~表5.3.5-2的技術(shù)要求。

a）在規(guī)定的試驗條件下進行低冰點瀝青混合料高溫動水沖刷實驗，并符合表5.3.5-1

的要求。

表5.3.5-1低冰點瀝青混合料高溫動水沖刷技術(shù)要求

性能要求

項目單位

基質(zhì)瀝青改性瀝青

殘留穩(wěn)定度比%280285

毛體積相對密度變化率%<1.0W0.8

b）必須在規(guī)定的試驗條件下進行低冰點瀝青混合料水穩(wěn)定性檢驗，并符合表5.3.5-2

的要求。

表5.3.5-2低冰點瀝青混合料水穩(wěn)定性技術(shù)要求

13

氣候條件與技術(shù)

相應(yīng)于以下氣候分區(qū)的技術(shù)要求

指標

試驗方法

年降雨量(mm)>1000500?1000250~500<250

氣候分區(qū)1.潮濕區(qū)2.濕潤區(qū)3.半干區(qū)4.干旱區(qū)

浸水馬歇爾試驗殘留穩(wěn)定度(酚，不小于

普通瀝青混合料8075JTG

改性瀝青混合料8580E20-2011T

SMA混合料800709

凍融劈裂試驗的殘留強度比(%),不小于

普通瀝青混合料7570JTG

改性瀝青混合料8075E20-2011T

SMA混合料800709

5.3.6宜對公稱最大粒徑大于或等于9.5mm,且小于16.0mm的低冰點瀝青混合料(含AC類、

SMA類)在規(guī)定試驗條件下進行低溫彎曲試驗，測定破壞應(yīng)變，其破壞應(yīng)變宜不小于表5.3.6

的技術(shù)要求。

表5.3.6低冰點瀝青混合料低溫性能技術(shù)要求

破壞應(yīng)變(Ue